钢齿牙轮钻头齿面强化复合堆焊实验研究

doi:10.3863/j.issn.1674-5086.2010.01.028

西南石油大学学报(自然科学版) ›› 2010, Vol. 32 ›› Issue (1): 141-144.DOI: 10.3863/j.issn.1674-5086.2010.01.028

钢齿牙轮钻头齿面强化复合堆焊实验研究

黄本生1,2;范舟2;唐安俊2;杨眉2;刘清友1

1.“油气藏地质及开发工程”国家重点实验室·西南石油大学，四川成都 610500；2.西南石油大学材料科学与工程学院，四川成都 610500

收稿日期:2009-01-09 修回日期:1900-01-01 出版日期:2010-02-20 发布日期:2010-02-20
通讯作者: 黄本生

EXPERIMENTAL STUDY ON COMPOSITE REPAIR WELDING ON STRENGTHENING THE SURFACE OF STEEL TOOTH ROLLER CONE BIT

HUANG Ben-sheng1，2;FAN Zhou2;TANG An-jun2;YANG Mei2;LIU Qing-you1

1.State Key Lab of Oil and Gas Reservoir Geology and Exploitation，Southwest Petroleum University，Chengdu Sichuan 610500，China；2.School of Materials Science and Engineering，Southwest Petroleum University，Chengdu Sichuan 610500，China

Received:2009-01-09 Revised:1900-01-01 Online:2010-02-20 Published:2010-02-20
Contact: HUANG Ben-sheng

摘要/Abstract

摘要：

运用自制的包含金属化的金刚石和硬质合金复合堆焊焊条，以O₂-C₂H₂焰为焊接热源进行堆焊，制备了含有金刚石的复合堆焊层。采用X射线衍射仪（XRD）、光学显微镜、材料性能实验机、动载磨料磨损实验机等实验手段和方法进行了金刚石表面和复合堆焊层形貌分析，堆焊层与基体的结合强度及堆焊层在动载荷条件下耐磨损性能的测试。研究表明：金刚石经过金属化处理后表面具有一定的金属性和浸润性，通过一定堆焊工艺在钢齿牙轮钻头齿面形成了组织致密均匀、硬质点与基体熔合良好的强化层，其抗剪强度达到了625MPa，磨损量减少了10％～70％，延长了钻头的使用寿命。

关键词: 钢齿牙轮钻头, 金刚石, 复合堆焊, 剪切强度, 耐磨性能

Abstract:

Composite repair welding layers with diamond are obtained by Repair Welding with Composite welding rod containing diamond and Carbide through O₂-C₂H₂ flaming.Morphology of composite repair welding layers and diamond surface after metalizing are analyzed with optical microscope and XRD，and bonding strength between repair welding layers and substrate and wear resistance of repair welding layers are tested by material testing machine and abrasion tester.The results show that diamond surface after metalizing has certain metallicity and wettability.The complex layers are compacted and wellproportioned，the shear strength of which is 625MPa and wear value is reduced by 10%～70%.The complex layers prolong the working life of steel tooth roller cone bit.

Key words: steel tooth roller cone bit, diamond, composite repair welding, shear strength, wear resistance

中图分类号:

TE921

黄本生;范舟;唐安俊;杨眉;刘清友. 钢齿牙轮钻头齿面强化复合堆焊实验研究[J]. 西南石油大学学报(自然科学版), 2010, 32 (1): 141-144.

HUANG Ben-sheng;FAN Zhou;TANG An-jun;YANG Mei;LIU Qing-you. EXPERIMENTAL STUDY ON COMPOSITE REPAIR WELDING ON STRENGTHENING THE SURFACE OF STEEL TOOTH ROLLER CONE BIT[J]. 西南石油大学学报(自然科学版), 2010, 32 (1): 141-144.

0
/ / 推荐

导出引用管理器 EndNote|Ris|BibTeX

链接本文: http://journal15.magtechjournal.com/Jwk_xnzk/CN/10.3863/j.issn.1674-5086.2010.01.028

http://journal15.magtechjournal.com/Jwk_xnzk/CN/Y2010/V32 /I1/141

[1]	杨眉刘清才高英薛屺黄本生 . 牙轮钻头强化用YQ4堆焊层组织性能研究[J]. 西南石油大学学报(自然科学版), 2010, 32(2): 169-172.
[2]	黄本生李西萍刘清友. 金刚石与碳化钨的复合堆焊[J]. 西南石油大学学报(自然科学版), 2003, 25(5): 71-73.
[3]	汤小文刘清友. 金刚石的盐浴镀钨 [J]. 西南石油大学学报(自然科学版), 1998, 20(4): 63-65.
[4]	汤小文　王子瑜　杨世良　陈菲. 金刚石与钢体的盐浴焊 [J]. 西南石油大学学报(自然科学版), 1997, 19(3): 73-77.
[5]	杨迎新侯季康林玉龙肖玉萍. 天然金刚石钻头CAD技术[J]. 西南石油大学学报(自然科学版), 1997, 19(2): 59-62.
[6]	刘清友陈良浩. 超硬工具材料CAN及其应用[J]. 西南石油大学学报(自然科学版), 1991, 13(3): 68-73.

钢齿牙轮钻头齿面强化复合堆焊实验研究

EXPERIMENTAL STUDY ON COMPOSITE REPAIR WELDING ON STRENGTHENING THE SURFACE OF STEEL TOOTH ROLLER CONE BIT

PDF (PC)

可视化

摘要/Abstract

引用本文

使用本文

参考文献

相关文章 6

编辑推荐

Metrics

本文评价