基于固体钙含量的CO2腐蚀水泥石规律预测

doi:10.11885/j.issn.16745086.2021.04.29.03

摘要/Abstract

摘要： CO₂会腐蚀油井水泥环，导致其强度衰退，使其失去保护套管和封隔油、气、水层的作用，从而缩短油气井寿命，造成巨大经济损失。如果能够预测CO₂在井下的腐蚀深度和腐蚀规律，那么就可以预测油井寿命，进而对水泥环耐腐蚀性能进行改进。然而，目前的CO₂腐蚀深度模型，大多是基于实验数据拟合建立的半经验模型，不具普遍适用性。针对这一问题，根据质量守恒定律结合扩散对流方程及钙离子沉淀速度，建立了CO₂腐蚀深度预测模型。该模型考虑了CO₂的扩散作用以及钙离子的沉淀，具有较强的适用性。通过CO₂腐蚀实验验证了该模型的可靠性，并利用该模型分析了水泥石基质被腐蚀后的变化规律，结果表明，随着腐蚀时间增加，水泥环孔隙度、渗透率增加，孔道迂曲度减小从而导致物质对流扩散加快、腐蚀速率加快；距离腐蚀端面越近孔隙度、渗透率越大，孔道迂曲度越小。

关键词: 油井水泥, CO₂, 钙离子, 腐蚀深度, 预测模型

Abstract: CO₂ will corrode the cement sheath of oil well, leading to its strength decline, make it lose the function of protecting casing and sealing off oil, gas and water. Thus shorten the life of oil and gas well and cause huge economic loss. If the corrosion depth and corrosion laws of CO₂ downhole can be predicted, the life of the oil well can be predicted, and the corrosion resistance of the cement ring can be improved. However, most of the current CO₂ corrosion depth models are semi empirical models based on experimental data fitting, which are not universally applicable. To solve this problem, a prediction model of CO₂ corrosion depth was established based on the law of mass conservation, diffusion convection equation and calcium precipitation rate. The model takes into account many factors, especially the diffusion of CO₂ and the precipitation of calcium ions, so it has strong applicability. The reliability of the model is verified by CO₂ corrosion test, and the change law of cement matrix change after corrosion is analyzed by using the model. The results show that with the increase of corrosion time, the porosity and permeability of cement sheath increase, and the tortuosity decreases, which leads to the acceleration of material convection diffusion and corrosion rate; the closer to the corrosion end, the greater the porosity and permeability, and the smaller the tortuosity.

Key words: oil well cement, CO₂, calcium ion, corrosion depth, prediction model

中图分类号:

TE21

袁彬, 袁坤峰, 徐璧华, 颜爽. 基于固体钙含量的CO₂腐蚀水泥石规律预测[J]. 西南石油大学学报(自然科学版), 2021, 43(4): 191-198.

YUAN Bin, YUAN Kunfeng, XU Bihua, YAN Shuang. Prediction of CO₂ Corrosion of Cement Paste Based on Solid Calcium Content[J]. Journal of Southwest Petroleum University(Science & Technology Edition), 2021, 43(4): 191-198.

0
/ / 推荐

导出引用管理器 EndNote|Ris|BibTeX

链接本文: http://journal15.magtechjournal.com/Jwk_xnzk/CN/10.11885/j.issn.16745086.2021.04.29.03

http://journal15.magtechjournal.com/Jwk_xnzk/CN/Y2021/V43/I4/191

参考文献

[1] NELSON E B, GUILLOT D, MARTHA D, et al. Well cementing[M]. 2nd ed. Texas:Schlumberger, 2006.
[2] 李玉飞,陈刚,张林,等. 高温高压酸性气藏镍基合金梯形缝衬管完井技术研究与应用——以龙王庙组气藏为例[C]. 福州:全国天然气学术年会, 2018. LI Yufei, CHEN Gang, ZHANG Lin, et al. Research and application of nickel base alloy trapezoidal fracture liner well completion technology in high temperature and high pressure acid gas reservoir:Taking Longwangmiao Formation gas reservoir as an example[C]. Fuzhou:National Natural Gas Academic Annual Conference, 2018.
[3] 薛丽娜,周小虎,严焱诚,等. 高温酸性气藏油层套管选材探析——以四川盆地元坝气田为例[J]. 天然气工业,2013,33(1):85-89. doi:10.3787/j.issn.1000-0976.2013.01.014 XUE Lina, ZHOU Xiaohu, YAN Yancheng, et al. Material selection of the production casing in high-temperature sour gas reservoirs in the Changxing Formation, Yuanba Gas Field, Northeastern Sichuan Basin[J]. Natural Gas Industry, 2013, 33(1):85-89. doi:10.3787/j.issn.1000-0976.2013.01.014
[4] 徐长贵,于海波,王军,等. 渤海海域渤中19-6大型凝析气田形成条件与成藏特征[J]. 石油勘探与开发, 2019, 46(1):25-38. doi:10.11698/PED.2019.01.03 XU Changgui, YU Haibo, WANG Jun, et al. Formation conditions and accumulation characteristics of Bozhong 19-6 large condensate gas field in offshore Bohai Bay Basin[J]. Petroleum Exploration and Development, 2019, 46(1):25-38. doi:10.11698/PED.2019.01.03
[5] 周仕明,王立志,杨广国,等. 高温环境下CO₂ 腐蚀水泥石规律的实验研究[J]. 石油钻探技术, 2008, 36(6):9-13. doi:10.3969/j.issn.1001-0890.2008.06.003 ZHOU Shiming, WANG Lizhi, YANG Guangguo, et al. Researches of CO₂ corrosion to cement stone at high temperature[J]. Petroleum Drilling Techniques, 2008, 36(6):9-13. doi:10.3969/j.issn.1001-0890.2008.06.003
[6] 姚晓,唐明述. 油井水泥石CO₂ 腐蚀的热力学条件[J]. 油田化学, 1999, 16(1):10-13. doi:10.3969/j.issn.1000-4092.1999.01.003 YAO Xiao, TANG Mingshu. Carbonation of oilwell cement sheath:A thermodyamical study[J]. Oilfield Chemistry, 1999, 16(1):10-13. doi:10.3969/j.issn.1000-4092. 1999.01.003
[7] 辜涛. 二氧化碳地质封存条件下固井水泥石腐蚀损伤与防护研究[D]. 成都:西南石油大学, 2017. GU Tao. Study on degraddation of oilwell cement and anticorrosion technology under CO₂ geological storage conditions[D]. Chengdu:Southwest Petroleum University, 2017.
[8] XU Bihua, YUAN Bin, WANG Yongqing, et al. Nanosilica-latex reduction carbonation-induced degradation in cement of CO₂ geological storage wells[J]. Journal of Natural Gas Science and Engineering, 2019, 65:237-247. doi:10.1016/j.jngse.2019.03.013
[9] LIN Yuanhua, ZHU Dajiang, ZENG Dezhi, et al. Experimental studies on corrosion of cement in CO₂ injection wells under supercritical conditions[J]. Corrosion Science, 2013, 74:13-21. doi:10.1016/j.corsci.2013.03.018
[10] 张聪,张景富,乔宏宇,等. CO₂ 腐蚀油井水泥石的深度及其对性能的影响[J]. 钻井液与完井液, 2010, 27(6):49-51. doi:10.3969/j.issn.1001-5620.-2010.06.014 ZHANG Cong, ZHANG Jingfu, QIAO Hongyu, et al. Corrosive depth and effect on oil well cement stone by CO₂[J]. Drilling Fluid & Completion Fluid, 2010, 27(6):49-51. doi:10.3969/j.issn.1001-5620.2010.06.014
[11] 张聪,张景富,彭邦洲,等. CO₂ 腐蚀油井水泥石的深度及预测模型[J]. 硅酸盐学报, 2010, 38(9):1782-1787. doi:10.14062/j.issn.0454-5648.2010.09.011 ZHANG Cong, ZHANG Jingfu, PENG Bangzhou, et al. Depth and prediction model of oilwell cement stone eroded by carbon dioxide[J]. Journal of the Chinese Ceramic Society, 2010, 38(9):1782-1787. doi:10.14062/j.issn.0454-5648.2010.09.011
[12] HOUST Y F, WITTMANN F H. Depth profiles of carbonates formed during natural carbonation[J]. Cement & Concrete Research, 2002, 32(12):1923-1930. doi:10.1016/S0008-8846(02)00908-0
[13] YANG Yuanguang, YUAN Bin, WANG Yongqing, et al. Carbonation resistance cement for CO₂ storage and injection wells[J]. Journal of Petroleum Science and Engineering, 2016, 146:883-889. doi:10.1016/j.petrol.2016.08.006
[14] PETER M A, MUNTEAN A, MEIER S A, et al. Competition of several carbonation reactions in concrete:A parametric study[J]. Cement and Concrete Research, 2008, 38(12):1385-1393. doi:10.1016/j.cemconres.2008.09.003
[15] GALLO Y L, BILDSTEINE O, BROSSE E. Coupled reaction-flow modeling of diagenetic changes in reservoir permeability, porosity and mineral compositions[J]. Journal of Hydrology, 1998, 209(1):366-388. doi:10.1016/S0022-1694(98)00183-8
[16] 张大翔. 抗CO₂ 腐蚀油井水泥浆体系研究及原理分析[J]. 西部探矿工程, 2017, 29(7):59-61. doi:10.3969/j.issn.1004-5716.2017.07.019 ZHANG Daxiang. Research and principle analysis of CO₂ corrosion resistant oil well cement slurry system[J]. WestChina Exploration Engineering, 2017, 29(7):59-61. doi:10.3969/j.issn.1004-5716.2017.07.019
[17] WAN Keshu, LI Yan, SUN Wei. Experimental and modelling research of the accelerated calcium leaching of cement paste in ammonium nitrate solution[J]. Construction and Building Materials, 2013, 40:832-846. doi:10.1016/j.conbuildmat.2012.11.066
[18] KOICHI M, TETSUYA I, TOSHIHARU K. Multi-scale modeling of concrete performance Integrated material and structural mechanics[J]. Journal of Advanced Concrete Technology, 2003, 1(2):91-126. doi:10.3151/jact.1.91
[19] MASON H E, FRANE W L D, WALSH S D C, et al. Chemical and mechanical properties of wellbore cement altered by CO₂-rich brine using a multianalytical approach[J]. Environmental Science & Technology, 2013, 47(3):1745-1752. doi:10.1021/es3039906
[20] PHUNG Q T, MAES N, JACQUES D, et al. Modelling the carbonation of cement pastes under a CO₂ pressure gradient considering both diffusive and convective transport[J]. Construction and Building Materials, 2016, 114:333-351. doi:10.1016/j.conbuildmat.2016.03.191
[21] PAPADAKIS V G, VAYENAS C G, FARDIS M N. Experimental investigation and mathematical-modeling of the concrete carbonation problem[J]. Chemical Engineering Science, 1991, 46(5):1333-1338. doi:10.1016/0009-2509(91)85060-B
[22] KUTCHKO B G, STRAZISAR B R, DZOMBAK D A,et al. Degradation of well cement by CO₂ under geologic sequestration conditions[J]. Environmental Science & Technology, 2007, 41(13):4787-4792. doi:10.1021/es062828c
[23] 熊钰丹,席方柱. CO₂ 对油井水泥腐蚀的研究进展[J]. 钻井液与完井液, 2011, 28(S1):69-71. doi:10.3969/j.issn.1001-5620.2011.z1.021 XIONG Yudan, XI Fangzhu. Research progress on corrosion of CO₂ to oil well cement[J]. Drilling Fluid & Completion Fluid, 2011, 28(S1):69-71. doi:10.3969/j.issn.1001-5620.2011.z1.021
[24] BUIL M, REVERTEGAT E, OLIVER J. A model of the attack of pure water or under saturated lime solution on cement[J]. Astm Spt, 1991, 1123:227-241. doi:10.1520/STP19554S
[25] NAKARAI K, ISHIDA T, MAEKAWA K. Modeling of calcium leaching from cement hydrates coupled with micropore formation[J]. Journal of Advanced Concrete Technology, 2006, 4(3):395-407. doi:10.3151/jact.4.395
[26] 陆沛青,刘仍光,杨广国,等. 增强油井水泥石抗二氧化碳腐蚀方法[J]. 材料科学与工程学报, 2020, 38(4):566-570. doi:10.14136/j.cnki.issn1673-2812.2020.04.009 LU Peiqing, LIU Rengguang, YANG Guangguo, et al. Methods of strengthening anti-CO₂ corrosion of oil well cement stone[J]. Journal of Materials Science and Engineering, 2020, 38(4):566-570. doi:10.14136/j.cnki.issn1673-2812.2020.04.009
[27] 万伟,陈大钧. 水泥石防CO₂、H₂S腐蚀性能的室内研究[J]. 钻井液与完井液, 2009, 26(5):57-59. doi:10.3969/j.issn.1001-5620.2009.05.019 WAN Wei, CHEN Dajun. Laboratory studies on the resistance of set cement to corrosion caused by CO₂ and H₂S[J]. Drilling Fluid & Completion Fluid, 2009, 26(5):57-59. doi:10.3969/j.issn.1001-5620.2009.05.019

基于固体钙含量的CO₂腐蚀水泥石规律预测

Prediction of CO₂ Corrosion of Cement Paste Based on Solid Calcium Content

RichHTML

PDF (PC)

可视化

摘要/Abstract

引用本文

使用本文

参考文献

相关文章 15

编辑推荐

Metrics

本文评价

[1]	钟仪华, 王淑宁, 罗兰, 杨金莲, 岳永鹏. 用深度学习挖掘油田开发指标预测模型的知识[J]. 西南石油大学学报(自然科学版), 2020, 42(6): 63-74.
[2]	黄诚, 潘雯晋. 基于机器学习的石油多峰模型研究及应用[J]. 西南石油大学学报(自然科学版), 2020, 42(6): 75-81.
[3]	贾怀存, 康洪全, 李明刚, 程涛, 侯波. 桑托斯盆地盐下CO₂聚集条件及对油气成藏影响[J]. 西南石油大学学报(自然科学版), 2020, 42(4): 66-72.
[4]	谢丹, 瞿利明, 池建萍, 陶武龙, 熊维莉. CO₂原油体系中的PR状态方程改进方法[J]. 西南石油大学学报(自然科学版), 2020, 42(4): 127-134.
[5]	陈祖华, 孙雷, 杨正茂, 郑永旺, 于晓伟. 苏北低渗透油藏CO₂驱油开发模式探讨[J]. 西南石油大学学报(自然科学版), 2020, 42(3): 97-106.
[6]	魏兵, 尚静, 蒲万芬, 卡杰特·瓦列里, 赵金洲. 超临界CO₂在致密油藏中的扩散前缘预测[J]. 西南石油大学学报(自然科学版), 2020, 42(2): 94-102.
[7]	张德平, 马锋, 吴雨乐, 董泽华. 用于CO₂注气驱的油井缓蚀剂加注工艺优化研究[J]. 西南石油大学学报(自然科学版), 2020, 42(2): 103-109.
[8]	陈立超, 王生维, 张典坤, 郭丁丁, 任龙锋. 陇东地区煤层气井油管柱腐蚀机理研究[J]. 西南石油大学学报(自然科学版), 2020, 42(1): 170-180.
[9]	成涛, 栾雪莹, 王雯娟, 刘鹏超, 吕新东. 高CO₂含量气藏物质平衡方程及其动储量评价[J]. 西南石油大学学报(自然科学版), 2020, 42(1): 140-146.
[10]	周明, 廖茂, 韩宏昌, 肖阳, 李辰. 页岩气低伤害超临界CO₂凝胶压裂液研究[J]. 西南石油大学学报(自然科学版), 2019, 41(6): 100-105.
[11]	雷霄, 代金城, 陈健, 韩鑫, 鲁瑞彬. 高CO₂含量天然气偏差因子影响研究[J]. 西南石油大学学报(自然科学版), 2019, 41(4): 120-126.
[12]	张智, 宋闯, 窦雪锋, 杨昆, 丁剑. CO₂吞吐井套管腐蚀规律及极限吞吐轮次研究[J]. 西南石油大学学报(自然科学版), 2019, 41(4): 135-143.
[13]	李乐, 朱倩谊, 陈小康. 纯水体系下水合物的生成及堵塞实验研究[J]. 西南石油大学学报(自然科学版), 2019, 41(4): 152-158.
[14]	张智, 刘金铭, 张华礼, 李玉飞, 罗伟. 注CO₂采油井油管柱腐蚀速率预测[J]. 西南石油大学学报(自然科学版), 2019, 41(2): 175-184.
[15]	陈强, 孙雷, 潘毅, 高玉琼. 页岩纳米孔内超临界CO₂、CH₄传输行为实验研究[J]. 西南石油大学学报(自然科学版), 2018, 40(5): 154-162.